DOI: 10.1063/1.365228. X-ray diffraction study of solid-state formation of metastable MoSi2 and TiSi2 during mechanical alloying

X-ray diffraction study of solid-state formation of metastable MoSi2 and TiSi2 during mechanical alloying

10.1063/1.365228

Crossref journal-article

AIP Publishing

Journal of Applied Physics (317)

Abstract

The formation of metastable C40–MoSi2 and C49–TiSi2 during the mechanical alloying of metal/silicon powder mixtures has been investigated by x-ray diffraction. The mechanical alloying of a Si-rich Mo/Si powder mixture results in the formation of both C11b–MoSi2 and C40–MoSi2. The C40–MoSi2 phase is metastable and transforms to C11b–MoSi2 after annealing at 850 °C. The mechanical alloying of a stoichiometric Ti/Si powder mixture leads to the incipient formation of C49–TiSi2 and the subsequent polymorphic transformation to C54–TiSi2. The lattice parameters of C49–TiSi2, as determined from a mechanically alloyed Ti/Si powder sample that has been annealed at 700 °C, are as follows: a0=3.56 Å, b0=13.57 Å, and c0=3.55 Å.

Bibliography

Yen, B. K. (1997). X-ray diffraction study of solid-state formation of metastable MoSi2 and TiSi2 during mechanical alloying. Journal of Applied Physics, 81(10), 7061â7063.

Authors 1

Bing K. Yen (first)

References 21 Referenced 21

{'key': '2024020219055694800_r1'}
10.1063/1.94213 / Appl. Phys. Lett. (1983)
{'key': '2024020219055694800_r3', 'first-page': '132', 'volume': '83', 'year': '1992', 'journal-title': 'Z. Metallkd.'} / Z. Metallkd. (1992)
10.1016/S0036-9748(88)80093-0 / Scr. Metall. (1988)
{'key': '2024020219055694800_r5'}
{'key': '2024020219055694800_r6', 'first-page': '5976', 'volume': '51', 'year': '1981', 'journal-title': 'J. Appl. Phys.'} / J. Appl. Phys. (1981)
10.1557/JMR.1990.2854 / J. Mater. Res. (1990)
10.1063/1.335263 / J. Appl. Phys. (1985)
10.1063/1.352018 / J. Appl. Phys. (1992)
10.1063/1.354602 / J. Appl. Phys. (1993)
{'key': '2024020219055694800_r11'}
10.1111/j.1151-2916.1996.tb08966.x / J. Am. Ceram. Soc. (1996)
10.1557/JMR.1993.1311 / J. Mater. Res. (1993)
{'key': '2024020219055694800_r14'}
{'key': '2024020219055694800_r15'}
{'key': '2024020219055694800_r16'}
{'key': '2024020219055694800_r17'}
10.1111/j.1151-2916.1956.tb15590.x / J. Am. Ceram. Soc. (1956)
{'key': '2024020219055694800_r19'}
10.1007/BF00918638 / Monatsch. Chem. (1961)
{'key': '2024020219055694800_r21'}

Dates

Type	When
Created	23 years, 1 month ago (July 26, 2002, 9:52 a.m.)
Deposited	1 year, 7 months ago (Feb. 2, 2024, 2:59 p.m.)
Indexed	2 months ago (July 4, 2025, 9:03 a.m.)
Issued	28 years, 3 months ago (May 15, 1997)
Published	28 years, 3 months ago (May 15, 1997)
Published Print	28 years, 3 months ago (May 15, 1997)

Funders 0

None

BibTeX

@article{Yen_1997, title={X-ray diffraction study of solid-state formation of metastable MoSi2 and TiSi2 during mechanical alloying}, volume={81}, ISSN={1089-7550}, url={http://dx.doi.org/10.1063/1.365228}, DOI={10.1063/1.365228}, number={10}, journal={Journal of Applied Physics}, publisher={AIP Publishing}, author={Yen, Bing K.}, year={1997}, month=may, pages={7061–7063} }

JSON

{
  "indexed": {
    "date-parts": [
      [
        2025,
        7,
        4
      ]
    ],
    "date-time": "2025-07-04T13:03:30Z",
    "timestamp": 1751634210813
  },
  "reference-count": 21,
  "publisher": "AIP Publishing",
  "issue": "10",
  "content-domain": {
    "domain": [
      "pubs.aip.org"
    ],
    "crossmark-restriction": true
  },
  "published-print": {
    "date-parts": [
      [
        1997,
        5,
        15
      ]
    ]
  },
  "abstract": "<jats:p>The formation of metastable C40\u2013MoSi2 and C49\u2013TiSi2 during the mechanical alloying of metal/silicon powder mixtures has been investigated by x-ray diffraction. The mechanical alloying of a Si-rich Mo/Si powder mixture results in the formation of both C11b\u2013MoSi2 and C40\u2013MoSi2. The C40\u2013MoSi2 phase is metastable and transforms to C11b\u2013MoSi2 after annealing at 850\u2009\u00b0C. The mechanical alloying of a stoichiometric Ti/Si powder mixture leads to the incipient formation of C49\u2013TiSi2 and the subsequent polymorphic transformation to C54\u2013TiSi2. The lattice parameters of C49\u2013TiSi2, as determined from a mechanically alloyed Ti/Si powder sample that has been annealed at 700\u2009\u00b0C, are as follows: a0=3.56\u2009\u00c5,\u2008b0=13.57\u2009\u00c5, and c0=3.55\u2009\u00c5.</jats:p>",
  "DOI": "10.1063/1.365228",
  "type": "journal-article",
  "created": {
    "date-parts": [
      [
        2002,
        7,
        26
      ]
    ],
    "date-time": "2002-07-26T13:52:35Z",
    "timestamp": 1027691555000
  },
  "page": "7061-7063",
  "update-policy": "http://dx.doi.org/10.1063/aip-crossmark-policy-page",
  "source": "Crossref",
  "is-referenced-by-count": 21,
  "title": "X-ray diffraction study of solid-state formation of metastable MoSi2 and TiSi2 during mechanical alloying",
  "prefix": "10.1063",
  "volume": "81",
  "author": [
    {
      "given": "Bing K.",
      "family": "Yen",
      "sequence": "first",
      "affiliation": [
        {
          "name": "Department of Materials Science and Metallurgy, University of Tokyo, Tokyo 113, Japan"
        }
      ]
    }
  ],
  "member": "317",
  "reference": [
    {
      "key": "2024020219055694800_r1"
    },
    {
      "key": "2024020219055694800_r2",
      "doi-asserted-by": "crossref",
      "first-page": "1017",
      "DOI": "10.1063/1.94213",
      "volume": "43",
      "year": "1983",
      "journal-title": "Appl. Phys. Lett."
    },
    {
      "key": "2024020219055694800_r3",
      "first-page": "132",
      "volume": "83",
      "year": "1992",
      "journal-title": "Z. Metallkd."
    },
    {
      "key": "2024020219055694800_r4",
      "doi-asserted-by": "crossref",
      "first-page": "1011",
      "DOI": "10.1016/S0036-9748(88)80093-0",
      "volume": "22",
      "year": "1988",
      "journal-title": "Scr. Metall."
    },
    {
      "key": "2024020219055694800_r5"
    },
    {
      "key": "2024020219055694800_r6",
      "first-page": "5976",
      "volume": "51",
      "year": "1981",
      "journal-title": "J. Appl. Phys."
    },
    {
      "key": "2024020219055694800_r7",
      "doi-asserted-by": "crossref",
      "first-page": "2854",
      "DOI": "10.1557/JMR.1990.2854",
      "volume": "5",
      "year": "1990",
      "journal-title": "J. Mater. Res."
    },
    {
      "key": "2024020219055694800_r8",
      "doi-asserted-by": "crossref",
      "first-page": "5240",
      "DOI": "10.1063/1.335263",
      "volume": "57",
      "year": "1985",
      "journal-title": "J. Appl. Phys."
    },
    {
      "key": "2024020219055694800_r9",
      "doi-asserted-by": "crossref",
      "first-page": "4978",
      "DOI": "10.1063/1.352018",
      "volume": "72",
      "year": "1992",
      "journal-title": "J. Appl. Phys."
    },
    {
      "key": "2024020219055694800_r10",
      "doi-asserted-by": "crossref",
      "first-page": "2954",
      "DOI": "10.1063/1.354602",
      "volume": "74",
      "year": "1993",
      "journal-title": "J. Appl. Phys."
    },
    {
      "key": "2024020219055694800_r11"
    },
    {
      "key": "2024020219055694800_r12",
      "doi-asserted-by": "crossref",
      "first-page": "2221",
      "DOI": "10.1111/j.1151-2916.1996.tb08966.x",
      "volume": "79",
      "year": "1996",
      "journal-title": "J. Am. Ceram. Soc."
    },
    {
      "key": "2024020219055694800_r13",
      "doi-asserted-by": "crossref",
      "first-page": "1311",
      "DOI": "10.1557/JMR.1993.1311",
      "volume": "8",
      "year": "1993",
      "journal-title": "J. Mater. Res."
    },
    {
      "key": "2024020219055694800_r14"
    },
    {
      "key": "2024020219055694800_r15"
    },
    {
      "key": "2024020219055694800_r16"
    },
    {
      "key": "2024020219055694800_r17"
    },
    {
      "key": "2024020219055694800_r18",
      "doi-asserted-by": "crossref",
      "first-page": "11",
      "DOI": "10.1111/j.1151-2916.1956.tb15590.x",
      "volume": "39",
      "year": "1956",
      "journal-title": "J. Am. Ceram. Soc."
    },
    {
      "key": "2024020219055694800_r19"
    },
    {
      "key": "2024020219055694800_r20",
      "doi-asserted-by": "crossref",
      "first-page": "781",
      "DOI": "10.1007/BF00918638",
      "volume": "92",
      "year": "1961",
      "journal-title": "Monatsch. Chem."
    },
    {
      "key": "2024020219055694800_r21"
    }
  ],
  "container-title": "Journal of Applied Physics",
  "original-title": [],
  "language": "en",
  "link": [
    {
      "URL": "https://pubs.aip.org/aip/jap/article-pdf/81/10/7061/18693857/7061_1_online.pdf",
      "content-type": "application/pdf",
      "content-version": "vor",
      "intended-application": "syndication"
    },
    {
      "URL": "https://pubs.aip.org/aip/jap/article-pdf/81/10/7061/18693857/7061_1_online.pdf",
      "content-type": "unspecified",
      "content-version": "vor",
      "intended-application": "similarity-checking"
    }
  ],
  "deposited": {
    "date-parts": [
      [
        2024,
        2,
        2
      ]
    ],
    "date-time": "2024-02-02T19:59:57Z",
    "timestamp": 1706903997000
  },
  "score": 1,
  "resource": {
    "primary": {
      "URL": "https://pubs.aip.org/jap/article/81/10/7061/2789/X-ray-diffraction-study-of-solid-state-formation"
    }
  },
  "subtitle": [],
  "short-title": [],
  "issued": {
    "date-parts": [
      [
        1997,
        5,
        15
      ]
    ]
  },
  "references-count": 21,
  "journal-issue": {
    "issue": "10",
    "published-print": {
      "date-parts": [
        [
          1997,
          5,
          15
        ]
      ]
    }
  },
  "URL": "http://dx.doi.org/10.1063/1.365228",
  "relation": {},
  "ISSN": [
    "0021-8979",
    "1089-7550"
  ],
  "subject": [],
  "published-other": {
    "date-parts": [
      [
        1997,
        5,
        15
      ]
    ]
  },
  "published": {
    "date-parts": [
      [
        1997,
        5,
        15
      ]
    ]
  }
}