DOI: 10.1063/1.1735005. Dislocation Sources in Crystals

10.1063/1.1735005

Crossref journal-article

AIP Publishing

Journal of Applied Physics (317)

Abstract

Lithium fluoride crystals were subjected to short stress pulses (1–10 μsec in length) in order to study dislocation nucleation in them. It was found that several heterogeneities can lead to dislocation nucleation: (a) cleavage steps, (b) dislocation loops, (c) glide bands, (d) inclusions or ``dirt'' particles, (e) precipitates (as grown), and (f) radiation-induced precipitates. Also, it was found that annealing treatments at moderate temperatures (200–600°C) followed by ``rapid'' cooling (&gt;5°C/hr) made segments of previously pinned dislocations become mobile. These mobile segments multiplied as they moved through the crystals. Several treatments were tried that were ineffective in producing dislocation nucleation. These included: temperature changes, surface wetting, simultaneous irradiation and stressing, reflections from free surfaces, and diagonal bending. Carefully cleaned glass spheres were pressed into contact with dislocation-free regions of a LiF crystal. In this way, shear stresses that were 100 times greater than the normal yield stress of the crystal (∼G/85) were reached without causing homogeneous dislocation nucleation. It is concluded that small foreign heterogeneities cause most of the dislocation nucleation in real crystals. Homogeneous nucleation occurs only at high stresses (∼G/30). Relatively little dislocation multiplication results from classical Frank-Read sources (almost none in LiF). Most dislocation multiplication occurs as a prior dislocation moves through a crystal.

Bibliography

Gilman, J. J. (1959). Dislocation Sources in Crystals. Journal of Applied Physics, 30(10), 1584â1594.

Authors 1

J. J. Gilman (first)

References 21 Referenced 131

10.1063/1.1712880 / J. Appl. Phys. (1941)
{'key': '2024020118443083000_r2'}
{'key': '2024020118443083000_r3'}
{'key': '2024020118443083000_r4'}
{'key': '2024020118443083000_r5'}
{'key': '2024020118443083000_r6', 'first-page': '449', 'volume': '209', 'year': '1957', 'journal-title': 'Trans. Am. Inst. Mining, Met., Petrol. Engrs.'} / Trans. Am. Inst. Mining, Met., Petrol. Engrs. (1957)
{'key': '2024020118443083000_r7', 'first-page': '524', 'volume': '240A', 'year': '1957', 'journal-title': 'Proc. Roy. Soc. (London)'} / Proc. Roy. Soc. (London) (1957)
10.1080/14786435808243219 / Phil. Mag. (1958)
{'key': '2024020118443083000_r9', 'first-page': '120', 'volume': '29', 'year': '1957', 'journal-title': 'J. Appl. Phys.'} / J. Appl. Phys. (1957)
10.1063/1.1735121 / J. Appl. Phys. (1959)
10.1063/1.1723322 / J. Appl. Phys. (1958)
{'key': '2024020118443083000_r12'}
{'key': '2024020118443083000_r13'}
10.1016/0022-3697(58)90176-8 / J. Phys. Chem. Solids (1958)
10.1063/1.1723277 / J. Appl. Phys. (1958)
{'key': '2024020118443083000_r16'}
{'key': '2024020118443083000_r17'}
{'key': '2024020118443083000_r18', 'first-page': '1068', 'volume': '28', 'year': '1957', 'journal-title': 'J. Appl. Phys.'} / J. Appl. Phys. (1957)
10.1080/14786435808244398 / Phil. Mag. (1958)
{'key': '2024020118443083000_r20'}
10.1063/1.1722931 / J. Appl. Phys. (1958)

Dates

Type	When
Created	20 years, 4 months ago (April 22, 2005, 12:14 p.m.)
Deposited	1 year, 7 months ago (Feb. 1, 2024, 2:05 p.m.)
Indexed	2 months ago (July 3, 2025, 2:28 a.m.)
Issued	65 years, 11 months ago (Oct. 1, 1959)
Published	65 years, 11 months ago (Oct. 1, 1959)
Published Print	65 years, 11 months ago (Oct. 1, 1959)

Funders 0

None

BibTeX

@article{Gilman_1959, title={Dislocation Sources in Crystals}, volume={30}, ISSN={1089-7550}, url={http://dx.doi.org/10.1063/1.1735005}, DOI={10.1063/1.1735005}, number={10}, journal={Journal of Applied Physics}, publisher={AIP Publishing}, author={Gilman, J. J.}, year={1959}, month=oct, pages={1584–1594} }

JSON

{
  "indexed": {
    "date-parts": [
      [
        2025,
        7,
        3
      ]
    ],
    "date-time": "2025-07-03T06:28:02Z",
    "timestamp": 1751524082154
  },
  "reference-count": 21,
  "publisher": "AIP Publishing",
  "issue": "10",
  "content-domain": {
    "domain": [
      "pubs.aip.org"
    ],
    "crossmark-restriction": true
  },
  "published-print": {
    "date-parts": [
      [
        1959,
        10,
        1
      ]
    ]
  },
  "abstract": "<jats:p>Lithium fluoride crystals were subjected to short stress pulses (1\u201310 \u03bcsec in length) in order to study dislocation nucleation in them. It was found that several heterogeneities can lead to dislocation nucleation: (a) cleavage steps, (b) dislocation loops, (c) glide bands, (d) inclusions or ``dirt'' particles, (e) precipitates (as grown), and (f) radiation-induced precipitates.</jats:p>\n               <jats:p>Also, it was found that annealing treatments at moderate temperatures (200\u2013600\u00b0C) followed by ``rapid'' cooling (&amp;gt;5\u00b0C/hr) made segments of previously pinned dislocations become mobile. These mobile segments multiplied as they moved through the crystals.</jats:p>\n               <jats:p>Several treatments were tried that were ineffective in producing dislocation nucleation. These included: temperature changes, surface wetting, simultaneous irradiation and stressing, reflections from free surfaces, and diagonal bending.</jats:p>\n               <jats:p>Carefully cleaned glass spheres were pressed into contact with dislocation-free regions of a LiF crystal. In this way, shear stresses that were 100 times greater than the normal yield stress of the crystal (\u223cG/85) were reached without causing homogeneous dislocation nucleation.</jats:p>\n               <jats:p>It is concluded that small foreign heterogeneities cause most of the dislocation nucleation in real crystals. Homogeneous nucleation occurs only at high stresses (\u223cG/30). Relatively little dislocation multiplication results from classical Frank-Read sources (almost none in LiF). Most dislocation multiplication occurs as a prior dislocation moves through a crystal.</jats:p>",
  "DOI": "10.1063/1.1735005",
  "type": "journal-article",
  "created": {
    "date-parts": [
      [
        2005,
        4,
        22
      ]
    ],
    "date-time": "2005-04-22T16:14:14Z",
    "timestamp": 1114186454000
  },
  "page": "1584-1594",
  "update-policy": "http://dx.doi.org/10.1063/aip-crossmark-policy-page",
  "source": "Crossref",
  "is-referenced-by-count": 131,
  "title": "Dislocation Sources in Crystals",
  "prefix": "10.1063",
  "volume": "30",
  "author": [
    {
      "given": "J. J.",
      "family": "Gilman",
      "sequence": "first",
      "affiliation": [
        {
          "name": "General Electric Research Laboratory, Schenectady, New York"
        }
      ]
    }
  ],
  "member": "317",
  "reference": [
    {
      "key": "2024020118443083000_r1",
      "doi-asserted-by": "crossref",
      "first-page": "100",
      "DOI": "10.1063/1.1712880",
      "volume": "12",
      "year": "1941",
      "journal-title": "J. Appl. Phys."
    },
    {
      "key": "2024020118443083000_r2"
    },
    {
      "key": "2024020118443083000_r3"
    },
    {
      "key": "2024020118443083000_r4"
    },
    {
      "key": "2024020118443083000_r5"
    },
    {
      "key": "2024020118443083000_r6",
      "first-page": "449",
      "volume": "209",
      "year": "1957",
      "journal-title": "Trans. Am. Inst. Mining, Met., Petrol. Engrs."
    },
    {
      "key": "2024020118443083000_r7",
      "first-page": "524",
      "volume": "240A",
      "year": "1957",
      "journal-title": "Proc. Roy. Soc. (London)"
    },
    {
      "key": "2024020118443083000_r8",
      "doi-asserted-by": "crossref",
      "first-page": "1",
      "DOI": "10.1080/14786435808243219",
      "volume": "3",
      "year": "1958",
      "journal-title": "Phil. Mag."
    },
    {
      "key": "2024020118443083000_r9",
      "first-page": "120",
      "volume": "29",
      "year": "1957",
      "journal-title": "J. Appl. Phys."
    },
    {
      "key": "2024020118443083000_r10",
      "doi-asserted-by": "crossref",
      "first-page": "129",
      "DOI": "10.1063/1.1735121",
      "volume": "30",
      "year": "1959",
      "journal-title": "J. Appl. Phys."
    },
    {
      "key": "2024020118443083000_r11",
      "doi-asserted-by": "crossref",
      "first-page": "877",
      "DOI": "10.1063/1.1723322",
      "volume": "29",
      "year": "1958",
      "journal-title": "J. Appl. Phys."
    },
    {
      "key": "2024020118443083000_r12"
    },
    {
      "key": "2024020118443083000_r13"
    },
    {
      "key": "2024020118443083000_r14",
      "doi-asserted-by": "crossref",
      "first-page": "14",
      "DOI": "10.1016/0022-3697(58)90176-8",
      "volume": "7",
      "year": "1958",
      "journal-title": "J. Phys. Chem. Solids"
    },
    {
      "key": "2024020118443083000_r15",
      "doi-asserted-by": "crossref",
      "first-page": "747",
      "DOI": "10.1063/1.1723277",
      "volume": "29",
      "year": "1958",
      "journal-title": "J. Appl. Phys."
    },
    {
      "key": "2024020118443083000_r16"
    },
    {
      "key": "2024020118443083000_r17"
    },
    {
      "key": "2024020118443083000_r18",
      "first-page": "1068",
      "volume": "28",
      "year": "1957",
      "journal-title": "J. Appl. Phys."
    },
    {
      "key": "2024020118443083000_r19",
      "doi-asserted-by": "crossref",
      "first-page": "125",
      "DOI": "10.1080/14786435808244398",
      "volume": "3",
      "year": "1958",
      "journal-title": "Phil. Mag."
    },
    {
      "key": "2024020118443083000_r20"
    },
    {
      "key": "2024020118443083000_r20a",
      "doi-asserted-by": "crossref",
      "first-page": "110",
      "DOI": "10.1063/1.1722931",
      "volume": "29",
      "year": "1958",
      "journal-title": "J. Appl. Phys."
    }
  ],
  "container-title": "Journal of Applied Physics",
  "original-title": [],
  "language": "en",
  "link": [
    {
      "URL": "https://pubs.aip.org/aip/jap/article-pdf/30/10/1584/18320506/1584_1_online.pdf",
      "content-type": "application/pdf",
      "content-version": "vor",
      "intended-application": "syndication"
    },
    {
      "URL": "https://pubs.aip.org/aip/jap/article-pdf/30/10/1584/18320506/1584_1_online.pdf",
      "content-type": "unspecified",
      "content-version": "vor",
      "intended-application": "similarity-checking"
    }
  ],
  "deposited": {
    "date-parts": [
      [
        2024,
        2,
        1
      ]
    ],
    "date-time": "2024-02-01T19:05:16Z",
    "timestamp": 1706814316000
  },
  "score": 1,
  "resource": {
    "primary": {
      "URL": "https://pubs.aip.org/jap/article/30/10/1584/162347/Dislocation-Sources-in-Crystals"
    }
  },
  "subtitle": [],
  "short-title": [],
  "issued": {
    "date-parts": [
      [
        1959,
        10,
        1
      ]
    ]
  },
  "references-count": 21,
  "journal-issue": {
    "issue": "10",
    "published-print": {
      "date-parts": [
        [
          1959,
          10,
          1
        ]
      ]
    }
  },
  "URL": "http://dx.doi.org/10.1063/1.1735005",
  "relation": {},
  "ISSN": [
    "0021-8979",
    "1089-7550"
  ],
  "subject": [],
  "published-other": {
    "date-parts": [
      [
        1959,
        10
      ]
    ]
  },
  "published": {
    "date-parts": [
      [
        1959,
        10,
        1
      ]
    ]
  }
}